What is the difference between Rogers RO4835 and Rogres RO4350B PCB sheets
The dielectric constant and dissipation factor of the Rogers RO4835 and Rogers RO4350B plates are basically the same. The difference is that the Rogers RO4835 plate adds an antioxidant filler to the Rogers RO4350B plate. It has passed the automotive safety test and is suitable for automotive anti-collision radars. Antenna products, radar ad onde millimetriche automobilistiche e altra elettronica automobilistica.
Rogers RO4350B and Rogers RO4835 both belong to Rogers RO4000 series hydrocarbon resin and ceramic filler PCB boards, which are civil materials. Entrambi i fogli sono compatibili con la pressione mista FR-4, FR-4 processing technology, and lead-free soldering process capabilities, garantire che gli impianti di elaborazione dei PCB debbano solo avere capacità di elaborazione inferiori e ridurre i costi di elaborazione dei PCB dei clienti.
The biggest difference between Rogers RO4350B and Rogers RO4835 is that Rogers RO4835 adds antioxidants. Compared with traditional thermosetting materials, the oxidation resistance is increased by 10 times, and it meets the requirements of IPC-4103 (substrate specifications for high-speed and high-frequency applications). Rogers RO4835 adds anti-oxidation material, which has stronger oxidation resistance than Rogers RO4350B. Fatta eccezione per la differenza tra Dk e Df, the temperature characteristics of Dk are relatively worse for products with glass cloth, e i requisiti per l'intervallo di temperatura del prodotto sono più elevati. The coefficient of thermal expansion becomes worse, especially in the z-axis, e il numero relativo di strati del prodotto diminuirà. The phase characteristics of high frequency are relatively worse, e i prodotti con requisiti rigorosi sulla fase dovrebbero essere evitati. The advantage is that the dimensional stability, durezza e assorbimento d'acqua del prodotto sono relativamente buoni.
Rogers Ro4835
The typical characteristics of Rogers RO4835 hydrocarbon ceramics are as follows:
1. Costante dielettrica 3.66
2. Dielectric loss 0.0037 1.0GHz
3. fattore di temperatura costante dielettrico 50ppm/
4. Glass transition temperature Tg>280 degrees
5. Cracking temperature Td390 degrees
6. Thermal conductivity 0.66w/m/k
7. Density 1..92gm/cm3
8. Grado antincendio UL94 V-0