PCB Technical - Causes of copper dumping on automotive circuit boards

The PCB copper wire falls off (also commonly referred to as dumping copper) is bad, and automobile circuit board factories all say that it is the problem of laminates and requires their production plants to bear the bad losses. According to experience, the common reasons for copper dumping in automotive circuit board factories are as follows:

1. PCB factory process factors:

1. Copper foil is over-etched. Electrolytic copper foil used in the market is generally single-sided galvanized (commonly known as ashing foil) and single-sided copper-plated (commonly known as red foil). Commonly thrown copper is generally galvanized copper above 70um. Foil, red foil and ash foil below 18um basically have no batch copper rejection.

When the customer circuit design is better than the etching line, if the copper foil specifications are changed but the etching parameters remain unchanged, the residence time of the copper foil in the etching solution is too long. Because zinc is originally an active metal, when the copper wire on the PCB is immersed in the etching solution for a long time, it will inevitably lead to excessive side corrosion of the circuit, causing some thin circuit backing zinc layer to be completely reacted and separated from the substrate. That is, the copper wire falls off.

Another situation is that there is no problem with the PCB etching parameters, but the copper wire is also surrounded by the remaining etching solution on the PCB surface after the etching, and the copper wire is also surrounded by the residual etching solution on the PCB surface. Throw the copper. This situation is generally manifested as concentrated on thin lines, or during periods of wet weather, similar defects will appear on the entire PCB. Strip the copper wire to see that the color of the contact surface with the base layer (the so-called roughened surface) has changed. The color of the copper foil is different from the normal copper foil. The original copper color of the bottom layer is seen, and the peeling strength of the copper foil at the thick line is also normal.

2. A collision occurs locally in the PCB process, and the copper wire is separated from the substrate by external mechanical force. This poor performance is poor positioning or orientation, the copper wire will be obviously twisted, or scratches/impact marks in the same direction. If you peel off the copper wire at the defective part and look at the rough surface of the copper foil, you can see that the color of the rough surface of the copper foil is normal, there will be no side erosion, and the peeling strength of the copper foil is normal.

3. The PCB circuit design is unreasonable, and the thick copper foil is used to design the thin circuit, which will also cause the circuit to be over-etched and the copper will be thrown away.

2. Reasons for laminate manufacturing process:

Under normal circumstances, the copper foil and the prepreg will be basically completely bonded as long as the high temperature section of the laminate is hot pressed for more than 30 minutes, so the pressing will generally not affect the bonding force of the copper foil and the substrate in the laminate. However, during the process of stacking and stacking laminates, if the PP is contaminated or the matte surface of the copper foil is damaged, the bonding force between the copper foil and the substrate after lamination will also be insufficient, resulting in positioning (only for large plates) Words) or sporadic copper wires fall off, but the peel strength of the copper foil near the disconnected wires will not be abnormal.

3. Reasons for laminate raw materials:

1. As mentioned above, ordinary electrolytic copper foils are all products that have been galvanized or copper-plated on wool. If the peak value of the wool foil is abnormal during production, or when galvanizing/copper plating, the plating crystal branches are bad, which will cause the copper foil itself. The peeling strength is not enough. After the bad foil pressed sheet material is made into a PCB, the copper wire will fall off when it is impacted by an external force when it is plugged in in the electronics factory. This type of copper rejection is not good. If you peel off the copper wire and see the rough surface of the copper foil (that is, the surface in contact with the substrate), there will be no obvious side erosion, but the peel strength of the entire copper foil will be very poor.

2. Poor adaptability of copper foil and resin: Some laminates with special properties, such as HTg sheets, are used now, because the resin system is different, the curing agent used is generally PN resin, and the resin molecular chain structure is simple. The degree of cross-linking is low, and it is necessary to use copper foil with a special peak to match it. When producing laminates, the use of copper foil does not match the resin system, resulting in insufficient peeling strength of the sheet metal-clad metal foil, and poor copper wire shedding when inserting.