Reliability test of PCBA lead-free solder joints

2021-10-21
View:515
Author:Downs

PCBA lead-free solder joint reliability test is mainly to conduct thermal load test (temperature shock or temperature cycle test) on electronic assembly products; perform mechanical stress test on electronic device joints according to fatigue life test conditions; use models for life evaluation.

Reliability test of PCBA lead-free solder joints

PCBA lead-free solder joint reliability test methods mainly include visual inspection, X-ray inspection, metallographic section analysis, strength (tensile, shear), fatigue life, high temperature and high humidity, drop test, random vibration, and reliability testing methods Wait. A few of them are introduced below:

1. Visual inspection

Lead-free and lead-free PCBA solder joints are different from the outside, and will affect the correctness of the AOI system. The stripes of PCBA lead-free solder joints are more obvious and rougher than the corresponding leaded solder joints, which are caused by the phase change from liquid to solid. Therefore, this type of solder joint looks rougher and uneven. In addition, due to the high surface tension of lead-free solder in PCBA processing, it is not as easy to flow as lead solder, and the rounded corners formed are not the same.

pcb board

2. X-ray inspection

In the spherical solder joints of PCBA lead-free soldering, the number of virtual soldering increases. PCBA lead-free solder has a higher soldering density, which can detect cracks and virtual soldering during soldering. Copper, tin and silver should be classified as "high-density" materials. In order to characterize the characteristics of good soldering, monitor the PCBA assembly process, and perform the most important PCBA solder joint structural integrity analysis, it is necessary to recalibrate the X-ray system. The testing equipment has higher requirements.

3. Metallographic section analysis

Metallographic analysis is one of the important methods of experimental research on metal materials. In PCBA solder joint reliability analysis, the metallographic structure of the solder joint profile is often taken for observation and analysis, so it is called metallographic section analysis. Metallographic section analysis is a destructive inspection. It has a long sample production cycle and high cost. It is often used for analysis after solder joint failures, but it has the advantages of being intuitive and speaking with facts.

4. Automatic solder joint reliability detection technology

Automatic solder joint reliability detection technology is an advanced technology that uses photothermal method to detect the quality of circuit board solder joints point by point. It has the characteristics of high detection accuracy, good reliability, and no need to touch or damage the tested solder joints during testing. During the inspection, certain laser energy is injected into the solder joints of the PCBA board point by point, and an infrared detector is used to monitor the thermal radiation generated by the solder joints after being irradiated by the laser. Since the heat radiation characteristics are related to the quality of the solder joints, the quality of the solder joints can be judged accordingly.

5. Perform temperature-related fatigue tests

In the PCBA lead-free process solder joint reliability test, the more important thing is the temperature-dependent fatigue test for the different thermal expansion coefficients of the solder joint and the connected components, including isothermal mechanical fatigue test and thermal fatigue test.

The most important point when evaluating the reliability of PCBA lead-free solder joints is to select the most relevant test method, and to clearly determine the test parameters for a specific method. In the PCBA lead-free process solder joint reliability test, it is more important to conduct temperature-dependent fatigue testing for the different thermal expansion coefficients of solder joints and connected components, including isothermal mechanical fatigue testing, thermal fatigue testing, and corrosion resistance testing. According to the test results, it can be confirmed that different lead-free materials have different resistance to mechanical stress at the same temperature. At the same time, studies have shown that different lead-free materials show different failure mechanisms and failure modes.